Electrodeposition of Zn-Ni alloy from non-cyanide alkaline sulphate bath containing triethanolamine (TEA) and mercaptopyridine (MPY) under optimized plating conditions such as bath pH, temperature current density and metal ion ratio in the bath produced an alloy deposit with the desired composition of 10-15 %wt. of nickel, alloy of this composition showed good adhesion, high hardness pore free, smooth, uniform and finer grained. Deposition potentials of Zn-Ni alloy lie between the potentials of individual metals. Increase in temperature density decreased the nickel content in the alloy deposit, which with increase in temperature and thickness of the alloy deposit increased nickel content in the alloy deposit. Alloy deposition followed a regular type of co-deposition.

Keywords: Triethanolamine; Electrodeposition; Zinc-Nickel Alloy; Cathodic Current Efficiency;